Zhuzhou Gold Sword Cemented Carbide Co., Ltd.
Decade of grinding sword
Add to Cart
YS2T tungsten steel strip, super-hard and ultra-fine grain, hardness above 92HRA,Superfine strips.
Definition of cemented carbide
Cemented carbide strips are mainly made by mixing WC tungsten carbide and Co cobalt powder through powder milling, ball milling, pressing and sintering by metallurgical methods. The main alloy components are WC and Co. The WC in carbide strips for different purposes The composition content of Co is not exactly the same, and the application range is extremely wide.
Cemented carbide strip is one of many materials, named after its rectangular plate (or square), also known as carbide strip.
Production technology
Pulverizing → formula according to application requirements → wet grinding → mixing → pulverizing → drying → sieving → adding forming agent → re-drying → sieving to obtain a mixture → granulating → pressing → forming → sintering → forming (blank) →Flaw inspection→Packing→Warehousing.
the advantages and application
Cemented carbide strips have the characteristics of high red hardness, good weldability, high hardness, and high wear resistance.
Mainly used in the production and processing of solid wood, density board, gray cast iron, non-ferrous metal materials, chilled cast iron, hardened steel, PCB, brake materials. When in use, you should select the carbide strip of suitable material according to the specific purpose.
Produsts measurement
| Uncommon Specifications | ||||||
| (T) | (W) | (L) | (T) | (W) | (L) | |
| mm | mm | mm | mm | mm | mm | |
| 0.8~1.5 | 1.0 | 20~320 | 1.5~2.0 | 1.0 | 20~320 | |
| 0.8~1.5 | 1.2 | 20~320 | 1.5~2.0 | 1.2 | 20~320 | |
| 0.8~1.5 | 1.4 | 20~320 | 1.5~2.0 | 1.4 | 20~320 | |
| 0.8~1.5 | 1.6 | 20~320 | 1.5~2.0 | 1.6 | 20~320 | |
| 0.8~1.5 | 1.8 | 20~320 | 1.5~2.0 | 1.8 | 20~320 | |
| 0.8~1.5 | 2 | 20~320 | 1.5~2.0 | 2 | 20~320 | |
| 0.8~1.5 | 2.2 | 20~320 | 1.5~2.0 | 2.2 | 20~320 | |
| 0.8~1.5 | 2.4 | 20~320 | 1.5~2.0 | 2.4 | 20~320 | |
| 0.8~1.5 | 2.6 | 20~320 | 1.5~2.0 | 2.6 | 20~320 | |
| 0.8~1.5 | 2.8 | 20~320 | 1.5~2.0 | 2.8 | 20~320 | |
Each Grade Meterial's Application
| GSGrade | ISO Grade | Density (g/cm3) | Hardness (HRA) | T.R.S (MPα) | Grain Size | Performance & Application Recommended |
| YG8 | K20 | 14.6-15.0 | 90~90.5 | 2200~2400 | Medium | High hardness, suitable for roughing of iron, solid wood, dry wood or nonferrous metal, ceramic and other alloys. |
| YL10.2 | K30 | 14.6-15.0 | 90~90.5 | 2600~2800 | Fine | High toughness, easy to be brazed without heat preservation. Suitable for rosewood, solid wood, pinewood, and other wood with a lot stammer. |
| YG6X | K10 | 14.6-15.0 | 92.5~93 | 1800-2000 | Ultrafine | High hardness, suitable for finishing of iron, nonferrous metal, ceramic and other alloying, semifinishing of of hardwood, chipboard, MDF and HDF. Better to use silver soldering. |
| YS2T | K40 | 14.5~14.6 | 87.5~88 | 2800~3000 | Fine | Contains a small amount of tantalum and niobium, high cobalt content, good toughness, good red hardness, suitable for processing and stainless steel. |
Products process